摘要：【中文】本发明公开了一种适用于餐桌的新型油漆及制备方法，包括以下重量份的原料：E‑20环氧树脂16‑26份、弹性树脂12‑25份、卡波姆2‑8份、酰胺改性氢化蓖麻油1‑9份、豆油卵磷酸2.5‑2.8份、四盐基铬酸锌2.5‑8.5份、OP‑10 0.7‑3.5份，甲苯二异氰酸酯3.5‑9份、硅藻土0.5‑4.5份，表面活性剂0.5‑1.9份、环烷酸锰5‑12份、水35‑50份。本发明与现有技术相比的优点在于：原材料价格低、有害化学品用量少，干燥后能形成连续性的油漆涂层，油漆涂层具有良好的延伸率及断裂强度，耐玷污性好，耐候性优异、施工方便、无环境污染，经济耐用，具有极强的普适性。 【EN】The invention discloses a novel paint suitable for dining tables and a preparation method thereof, wherein the paint comprises the following raw materials in parts by weight: 16-26 parts of E-20 epoxy resin, 12-25 parts of elastic resin, 2-8 parts of carbomer, 1-9 parts of amide modified hydrogenated castor oil, 2.5-2.8 parts of soybean oil lecithin, 2.5-8.5 parts of zinc chromate tetrabasic, 100.7-3.5 parts of OP-100, 3.5-9 parts of toluene diisocyanate, 0.5-4.5 parts of kieselguhr, 0.5-1.9 parts of surfactant, 5-12 parts of manganese naphthenate and 35-50 parts of water. Compared with the prior art, the invention has the advantages that: the raw materials are low in price, the dosage of harmful chemicals is small, a continuous paint coating can be formed after drying, and the paint coating has the advantages of good elongation percentage and breaking strength, good stain resistance, excellent weather resistance, convenience in construction, no environmental pollution, economy and durability, and strong universality.

摘要：【中文】本发明公开了一种用于家具的水性漆，其特征在于：制备步骤如下：(1)将松木用240#砂纸打磨，均匀擦涂水性封筋剂，其用量70‑90g/m2，让水性封筋剂渗入底材迅速与木质纤维结合，让伏倒的粗质纤维或木筋涨起；(2)三小时后用320#砂纸打磨，再均匀喷涂水性抗单宁酸封闭底漆，其用量145‑160g/m2，防止松木的黄变，以及高温下油脂外冒；(3)两小时后用320#砂纸打磨，最后均匀喷涂水性面漆，其用量100‑120g/m2，即可完成施工，取样、检测、出料、入库，木器表面在75℃条件下不回粘，手感好。本发明与现有技术相比的优点在于：粘结性能高，力学性能好，大大提高其抗划伤性和高温抗回粘性，施工操作方便等优点。 【EN】The invention discloses a water-based paint for furniture, which is characterized in that: the preparation steps are as follows: (1) grinding pine wood by using No. 240 abrasive paper, uniformly wiping and coating the water-based bar sealing agent with the dosage of 70-90g/m2, so that the water-based bar sealing agent permeates into a substrate and is rapidly combined with wood fibers, and the fallen coarse fibers or wood bars are swelled; (2) grinding the pine wood by using 320# abrasive paper after three hours, and uniformly spraying the water-based anti-tannic acid seal primer with the dosage of 145-160g/m2 to prevent the pine wood from yellowing and prevent the grease from overflowing at high temperature; (3) and after two hours, grinding by using No. 320 abrasive paper, and finally uniformly spraying the water-based finish paint with the dosage of 100 plus one 120g/m2 to finish construction, sampling, detecting, discharging and warehousing, wherein the surface of the woodware is not sticky back under the condition of 75 ℃, and the hand feeling is good. Compared with the prior art, the invention has the advantages that: high adhesion and mechanical performance, greatly improved scratch resistance and high-temperature anti-sticking property, convenient construction and operation, etc.