摘要：【中文】本发明提供了一种易清除的玻璃印刷油墨的制备方法，包括：准备颜料；准备油墨连结料；配料：选用高温油墨和钢化油墨按照质量比为1:7的配比进行调配油墨；搅拌：将颜料、油墨连结料、油墨和助剂按量称取，并放入调和桶中，用搅拌机进行搅拌，搅拌的速度开始较低，以防止色粉飞扬，然后再高速搅拌至油墨料调和成糊状；轧研：通过研磨机对糊状的油墨料进行研轧时，使油墨连结料中的颜料分散；混合：在轧墨之后，还需要将部分溶剂、调墨油和助剂与已轧细的墨料混合均匀，至达到要求的黏度，制得油墨。本发明所制备的油墨在玻璃上实现了良好的印刷和热转印，经过600℃高温后可从玻璃上清除下来，可实现回收使用，经济环保。 【EN】The invention provides a preparation method of glass printing ink easy to remove, which comprises the following steps: preparing a pigment; preparing an ink vehicle; preparing materials: selecting high-temperature ink and toughened ink to mix the ink according to the mass ratio of 1: 7; stirring: weighing the pigment, the ink binder, the ink and the auxiliary agent according to the amount, putting the weighed pigment, the ink binder, the ink and the auxiliary agent into a blending barrel, stirring the mixture by using a stirrer at a low stirring speed to prevent the toner from flying, and then stirring the mixture at a high speed until the ink binder is blended into paste; rolling and grinding: dispersing the pigment in the ink vehicle when the pasty ink vehicle is ground and rolled by a grinder; mixing: after ink rolling, part of the solvent, the ink adjusting oil and the auxiliary agent are required to be uniformly mixed with the rolled ink material until the required viscosity is reached, so that the ink is prepared. The ink prepared by the invention realizes good printing and heat transfer printing on glass, can be removed from the glass after being subjected to high temperature of 600 ℃, can be recycled, and is economic and environment-friendly.