摘要：【中文】本发明一种纯棉缎纹面料仿真丝整理剂及制备方法，由氨基聚醚改性聚有机硅氧烷，季铵化聚醚嵌段聚有机硅氧烷，免烫树脂整理剂，非离子聚氨酯乳液组成，用于纯棉缎纹面料的后整理后具有真丝面料般的手感及光泽，织物的外观平整度可以达到3级以上，起毛起球达到3级以上。 【EN】The invention relates to a pure cotton satin fabric silk-like finishing agent and a preparation method thereof, which consists of amino polyether modified polysiloxane, quaternized polyether block polysiloxane, a non-ironing resin finishing agent and nonionic polyurethane emulsion, and has the hand feeling and the luster of a pure cotton satin fabric after being used for after-finishing, the appearance flatness of the fabric can reach more than 3 grades, and the fuzzing and pilling can reach more than 3 grades.

摘要：【中文】本发明一种纺织品用水性透湿、阻燃聚氨酯乳液及制备方法，由异佛尔酮二异氰酸酯、氢化MDI、环氧乙烷和四氢呋喃共聚醚多元醇、聚已内酯多元醇、阻燃聚酯多元醇、环氧乙烷和四氢呋喃共聚醚多元醇、扩链剂、小分子扩链剂、有机硅多元醇、去离子水经预聚反应、扩链反应、乳化反应、扩链反应、封闭反应制成；其成膜柔软、弹性好、干爽，同时达到透湿好、阻燃好、耐寒好、耐水压高、断裂强力大、耐洗牢度好、断裂伸长率高。可通过复配助剂使用离型纸或OPP制成膜制品，或通过复配助剂制成纺织品涂层胶，对棉、尼龙、涤纶面料涂层处理使用。 【EN】The invention relates to an aqueous moisture permeable and flame retardant polyurethane emulsion for textiles and a preparation method thereof, wherein the emulsion is prepared by carrying out prepolymerization reaction, chain extension reaction, emulsification reaction, chain extension reaction and sealing reaction on isophorone diisocyanate, hydrogenated MDI, ethylene oxide and tetrahydrofuran copolymerized polyether polyol, polycaprolactone polyol, flame retardant polyester polyol, ethylene oxide and tetrahydrofuran copolymerized polyether polyol, a chain extender, a small molecular chain extender, organic silicon polyol and deionized water; the film is soft, good in elasticity and dry and comfortable, and simultaneously achieves the purposes of good moisture permeability, good flame retardance, good cold resistance, high water pressure resistance, large breaking strength, good washing fastness and high elongation at break. The film product can be prepared by using release paper or OPP through a compound auxiliary agent, or the textile coating adhesive can be prepared by using the compound auxiliary agent, and the film product can be used for coating treatment of cotton, nylon and polyester fabrics.

摘要：【中文】本发明一种纺织品用水性防水透湿、阻燃聚氨酯膜及制备方法，由异佛尔酮二异氰酸酯、氢化MDI、环氧乙烷和四氢呋喃共聚醚多元醇、聚已内酯多元醇、阻燃聚酯多元醇、环氧乙烷和四氢呋喃共聚醚多元醇、扩链剂、小分子扩链剂、有机硅多元醇、去离子水经预聚反应、扩链反应、乳化反应、扩链反应、封闭反应制成乳液，在复配消泡剂、润湿流平剂、滑爽剂、增稠剂、消光剂、脱模剂、交联剂制成膜胶，涂层在离型纸或OPP上烘干，制得纺织品用水性透湿阻燃聚氨酯膜制品。其成膜柔软、弹性好、干爽，同时达到透湿好、阻燃好、耐寒好、耐水压高、断裂强力大、耐洗牢度好、断裂伸长率高。 【EN】The invention relates to a water-based waterproof moisture-permeable flame-retardant polyurethane film for textiles and a preparation method thereof. The film is soft, good in elasticity and dry and comfortable, and simultaneously achieves the purposes of good moisture permeability, good flame retardance, good cold resistance, high water pressure resistance, large breaking strength, good washing fastness and high elongation at break.